Catalyst design for VRLA batteries

ABSTRACT

A catalyst device for use with battery cells to recombine oxygen and hydrogen gas and thereby improve the performance and life of such cells. The catalyst device has the ability to filter out catalyst poisons and control the temperature of the recombination reactions. A container houses the catalyst within a chamber. A catalyst poison filter is provided in the chamber with the catalyst. The movement of gas and vapor to and from the chamber is controlled by a microporous section of the device. The pore size is chosen to allow gas and vapor to pass, but not liquids, and to also prevent a flame from passing through. Within these parameters the pore size can also be chosen to control and or limit the amount of gas that can pass through to the catalyst in a given time period. Preferably, the microporous section is formed as a disc that seals an opening in the chamber. The filter material is then placed as a layer between the catalyst and the opening such that the poison in the gas must pass through the filter material before reaching the catalyst.

CROSS REFERENCE TO RELATED APPLICATION

[0001] This application claims the benefit of U.S. Provisional Applications No. 60/112,305 filed Dec. 14, 1998, No. 60/113,579 filed Dec. 24, 1998, and No. 60/148,536 filed Aug. 12, 1999, all of which are hereby incorporated by reference.

BACKGROUND

[0002] 1. Field of the Invention

[0003] The present invention relates to the use of catalysts for improving the service life of valve regulated lead acid (VRLA) cells, and to a catalyst device which may also be applicable to other types of batteries where it is desirable to recombine excess oxygen with hydrogen produced in the battery cell. More particularly, the present invention relates to improved catalyst devices that minimize catalyst poisoning and control the temperature of the catalytic reaction.

[0004] 2. Background of the Invention

[0005] Significant improvements to VRLA battery cells can be made with the addition of a catalyst for recombining oxygen and hydrogen gasses within the cells as disclosed in U.S. application Ser. No. 09/022,336 filed Feb. 11, 1998, and which is hereby incorporated by reference. One preferred method of adding catalyst to VRLA cells is to couple the catalyst with the pressure relief vent, i.e., the “valve”, which provides a convenient means of retrofitting existing cells as well adding catalyst to new cells. A novel catalyst device for use with pressure relief vents is disclosed in U.S. application Ser. No. 09/022,336. While the addition of catalyst provides significant improvement in the performance and of life of VRLA cells, additional improvements to the catalyst itself, particularly with the structures and devices that support or house the catalyst, are believed necessary to gain the full benefits of the catalyst.

[0006] High rates of gassing in VRLA battery cells can be caused by conditions such as thermal runaway, malfunctioning power rectifiers, boost charging, charging at abnormally high rates of voltage, and other reasons known in the art. In lead-acid battery cells, oxygen and hydrogen gas is generated due to the electrolysis of water. If a catalyst were installed in a cell experiencing a high rate of gas production, the catalyst would catalyze the oxygen and hydrogen to water in a highly exothermic reaction. The resulting enthalpy could generate enough heat to melt many commonly used plastic materials that compose the battery cover, jar or vent cap assemblies. This high reaction temperature can also limit the materials that can be used to house the active catalytic material.

[0007] One catalyst device as described in the above referenced U.S. application Ser. No. 09/022,336 patent application, uses a porous ceramic cartridge to house the catalytic active material. This porous cartridge allows gas to enter the chamber and water vapor to exit the chamber, and prevents the passing of a flame from inside the chamber to outside the chamber if one were to develop due to ignition of the gases. The temperature achieved, as a result of the exothermic reaction, is governed mainly by the amount of gas produced by the battery. In the normal functioning of a VRLA battery, the temperature of reaction is generally not more than 5° to 10° F. above ambient temperature. However, in the case of high rates of gassing, a higher than normal temperature could occur which could lead to melting of the plastic that supports the catalyst cartridge, that composes the vent cap or that composes the cell jar or cell cover. The high temperature could also deform the pressure relief valve that is present in the vent cap for these VRLA cells. A deformed pressure relief valve will change the operating characteristics of the cell. Temperature high enough to melt the plastics used to compose batteries must be avoided.

[0008] Another problem found to plague lead acid cells is catalyst poisoning. Precious metal catalysts, such as palladium and platinum are susceptible to poisoning by many chemicals that can limit and negate the effectiveness of the catalysts. Catalyst poisons can be generated in or found in the battery cells. VRLA batteries are constructed of materials that may exhaust gaseous compounds that are poisonous to catalysts. Such poisons include organic compounds such as phalates used as a plasticizer in PVC battery jars and covers, and inorganic compounds such as sulfides, mercaptins, amines, stibine and phosphates whose base chemicals can exist as an impurity in battery plates and exhaust as the plates corrode. Amines and mercaptins are used extensively as curing compounds in multi-part epoxies which are used in the manufacture of cells by many manufacturers. It is also believed that localized areas of high current densities may cause hydrogen sulfide to form within the cells. Hydrogen sulfide may also be a byproduct of the dry charging process that traps sulfur species in the plates which is then released early in the battery's life. It is believed that compounds such as those described above that have a (−2) state of charge can bond with catalyst activation sites rendering the catalyst ineffective. The catalyst can also be poisoned by large chain molecules, such as phalates, that coat the catalyst substrate and then solidifying on it, creating a barrier that prevent the gasses from reaching the catalyst reaction sites. Hydrogen sulfide, SOX species, and other sulfides will also poison precious metal catalysts.

[0009] It is further believed that simpler and lower cost catalyst devices are desirable.

[0010] Accordingly, one object of the present invention is to limit the temperature of the catalytic reaction.

[0011] Another object of the present invention is to prevent poisoning of the catalyst.

[0012] Another object is to lower the manufacturing costs of catalyst devices.

SUMMARY OF THE INVENTION

[0013] In accordance with the present invention there is provided a device for combining oxygen and hydrogen gases within a battery cell. The device has a container which has a chamber. Arranged within the chamber is a catalyst capable of combining oxygen and hydrogen gases to form water vapor. The device includes a microporous section having pores through which gases in the battery cell can pass into the chamber to the catalyst. A catalyst poison filter is arranged in the device to remove at least some of the catalyst poisons in the gas passing through the filter to the catalyst.

[0014] The pore size and developed surface area can be chosen to control the temperature of the catalytic reaction by controlling the amount of gas that can pass through to the catalyst at any given time.

[0015] The container is preferably made of a non-porous plastic material and has an opening to the chamber. Sealing the opening is the microporous section formed as a microporous member. The filter material here is ideally placed in the chamber between the catalyst and the microporous member. This forces the gas entering the chamber through the microporous member to pass first through the filter before reaching the catalyst and thereby maximizes the effectiveness of the filter. This design presents an embodiment that combines both poison filtering and temperature control in one easy to manufacture, low cost and inherently safe to the cell design. It operates on the principle that the heat of reaction, of the catalyst, can be controlled by limiting the amount of oxygen and hydrogen gas that is exposed to the catalyst. This control is accomplished by selecting the proper pore size, developed and planar surface area, and/or wall thickness of the area that the hydrogen and oxygen pass through in the container that houses the catalyst. This area is created from a porous high temperature acid resistant plastic material that has inherent hydrophobic properties with a porosity that is small enough to not allow a hydrogen flame front to pass through (Anti-Flame Protection). The hydrogen and oxygen gasses will then pass through the filter bed that will remove any catalyst poisons before they reach the active material.

[0016] Other embodiments of the invention are also provided such as providing the microporous section in the container wall.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017]FIG. 1 is a cross sectional view of a device in accordance with the present invention having a flange;

[0018]FIG. 1A is an exploded view of the device of FIG. 1;

[0019]FIG. 1B is perspective view of the device of FIG. 1 attached to a pressure relief vent cap;

[0020]FIG. 2 is a perspective view of a flangless catalyst device held to a pressure relief vent by a holder;

[0021]FIG. 2A is a perspective view of the holder of FIG. 2;

[0022]FIG. 2B is a perspective view of the catalyst device of FIG. 2;

[0023]FIG. 3 is a top perspective view of a vent boss of a Monoblock type battery cell showing the top of a ¼ amp embodiment of the invention installed in the vent opening;

[0024]FIG. 3A is an exploded view of the ¼ amp device of FIG. 3;

[0025]FIG. 4 is a frontal view of another embodiment of the catalyst device;

[0026]FIG. 5 is a cross sectional view of another embodiment of the present invention;

[0027]FIG. 6 is a cross sectional view of yet another embodiment of the present invention;

[0028]FIG. 7 is a cross sectional view of another embodiment of the present invention; and

[0029]FIG. 8 is a schematic view of a VRLA battery cell in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0030] With reference to FIGS. 1, 1A and 1B, a catalyst device 10 is configured for attachment to a pressure relief vent 12 (FIG. 1B) of the type used with VRLA battery cells. The device 10 has a cylindrically shaped container 14 and is attached to an integral flange 16. The container 14 has a wall 18 defining an internal chamber 20. An opening 22 at the upper end of the container 14 permits access to the chamber 20 as described below. The container 14 is preferably made of high temperature plastic material resistant to sulfuric acid and suitable for the internal environment of a battery cell. The container material of this embodiment should also be impermeable to liquids and gases so that the gases can enter the chamber 22 only through the opening 20. A preferred material is Questra® made by Dow Chemical.

[0031] The flange 16 is integral to the container 14 and configured to fit a particular pressure relief vent 12. For pressure relief vents of other manufacturers, a flange configured specifically for the particular vent is readily provided by changing the mold insert in conjunction with the mold for the container 14. Here, the flange is configured to snap to the pressure relief valve 12 as shown, the flange in FIG. 1B having holes 24 for receiving snap pins 24 a of the vent 12. Means of attachment other than a snap type connection may be used. For example, the pins 24 a could be non-snap type pins that are inserted into holes 24 of the of the flange, and then the ends of the pins 24 are melted such as by heat staking or ultra sonic means to fix the container 14 to the pressure relief vent 12.

[0032] The chamber 22 contains a catalyst 26 for combining oxygen gas and hydrogen gas. Precious metal catalyst such a palladium and platinum may be used, a catalyst 26 of one-half percent palladium impregnated on an activated carbon substrate being preferred for the illustrated embodiment. It is understood that the uniform spheres representing the catalyst 26 as shown in the drawings are for illustrative purposes, the catalyst capable of being provided in many forms such as granules or fine powder.

[0033] Positioned between the catalyst 26 and the chamber opening 20, is a poison filter 28 for removing compounds that are poisonous to the catalyst. Suitable filter materials for the type of poisons found in VRLA cells include activated carbon, potassium carbonate (K₂CO₃), metals such a nickel, ruthenium, copper, and metal salts. A combination of multiple filter materials are preferred as some filter materials have a higher affinity or are more specific to particular poisons. In the illustrated embodiment, a multiple filter bed of 325 mesh activated carbon impregnated with 20% K₂CO₃ is preferred.

[0034] For poisons that are basic, the filter materials can be treated by soaking with {fraction (1/10)} molar HCL (hydrochloric acid) then drying at 180° F. for 24 hours to create an acidic filter having a strong affinity to react with basic poisons. For acidic poisons, the filter materials can be treated by soaking with a 5% sodium bicarbonate and water solution then drying at 180° F. for 24 hours to create an alkaline filter that will have a stronger affinity to react with acidic poisons.

[0035] The device 10 has a micro-porous section 30 through which the gas and vapor can pass between the chamber 22 and the environment outside the device 10 (the internal environment of the battery cell). In the present embodiment the microporous section 30 takes the form of disk shaped microporous member 30 a covering the opening 20 as shown which is fixed on a shoulder 32 formed in the container 14. The microporous disk member 30 a is heat sealed or ultrasonically welded in place see the angled edge 34 where the container was melted as part of the welding or heat staking process. The microporous member 30 is made of a porous material, preferably plastic, such as PVDF (polyvinylidene fluoride), PTFE (polytetrafluoroethylene) or polypropylene, and which is preferably hydrophobic in nature to water and the electrolyte (sulfuric acid in lead acid cells) in the battery cell. The pore size is such that only gas or vapor can pass through, but liquid will not. Likewise, the microporous section 30 should have a pore size small enough to not allow a hydrogen flame front to pass through. When the microporous member 30 a is sealed in place in the opening 10, the catalyst 26 is completely sealed within the chamber 22 such that gas or vapor can pass between the chamber 22 and the environment outside the device 10 only by passing through the pores of the microporous section 30 (disc 30 a).

[0036] The benefit of positioning the filter 28 between the catalyst 26 and microporous disk member 30 a is readily seen. Gases entering the chamber 20, which may include compounds poisonous to the catalyst, reach the catalyst only after passing through the filter 28. It is possible to provide a mixture of the catalyst and filter within the chamber 22 rather than the stratified layers shown. Some poisons, however, have a stronger affinity for the catalyst than the filter material, and, where the filter material and catalyst are near each other, may go to and poison the catalyst rather than to the filter. The illustrated embodiment avoids this problem by forcing the poison first through the filter.

[0037] The present invention also permits control of the heat of reaction in the catalyst by limiting the amount of oxygen and hydrogen gas that is exposed to the catalyst 26. As previously discussed, the pore size in the microporous section 30 is chosen such that only gas or vapor is capable of passing through, and to also act as an anti-flame barrier. Additionally, the pore size ultimately selected, in conjunction with other variables such as the planar surface area and the thickness of the microporous member 30 a is chosen to control the amount or rate of gas that can pass into the chamber 22 and subsequently be exposed to the catalyst 26. This exposure determines the heat of reaction that is generated by the catalyst action of combining the oxygen and the hydrogen gases into water. Pore sizes that are known to work as a method of temperature control are, but not limited to, 1 to 40 microns. Varying the thickness of the microporous member 30 in conjunction with selecting pore size can also be used to control temperature.

[0038] In the illustrated embodiment of FIGS. 1, 1A, and 1B, a preferred configuration has a cylindrical chamber 22 having a volume of approximately 0.35 cubic inches (with internal diameter of 0.45 inches). The volume of catalyst 26 (½% palladium on an activated carbon substrate) is about 0.12 cubic inches; the volume of filter material 28 (325 mesh activated carbon impregnated with 20% K₂CO₃) is about 0.23 cubic inches. The catalyst 26 and filter 28 materials completely fill the chamber 22 and are held tightly within by the microporous disk 30 a so that there is minimal movement and mixing of the materials even if the device 10 is shaken. It is seen that this embodiment has a ratio of 1/3 catalyst to 2/3 filter material by volume.

[0039] The disk-shaped microporous member 30 is formed of PTFE, ⅛″ inch thick, ½ inch diameter, and having a 25 micron pore size. This configuration provides a device 10 rated for about 1 Amp Faraday: 11-12 ml/minutes at standard temperature and pressure of 2 parts H₂ and 1 part O₂ passing through to the catalyst, and which generate a temperature in the range of 120° F. to 140° F. at these conditions.

[0040] In addition to providing temperature and poison control, the present invention also provides a simpler design over previous designs. One previous design uses a porous ceramic chamber that provided anti-flame protection and which was is externally wrapped with a hydrophobic PTFE film to protect the internal catalyst from liquid. The PTFE film has a specific porosity that allows hydrogen, oxygen and gaseous water to pass through, but does not allow any liquids to contact the catalyst. The present invention uses technology (the micro-porous section 30) that is inherently hydrophobic, anti-flame preventing, and microporous thus eliminating the need for the film and ceramic chamber while still serving the same functions. This results in a simpler and lower cost design.

[0041] The present invention is also adaptable to the many different battery cells and pressure relief vents of the different manufacturers. As previously discussed, the flange 16 is formed to specifically fit the vent 12 shown if FIG. 1B. The basic container 14 can be standardized and produced with a mold designed to accept inserts for creating flanges configured to fit vents made by other manufacturers. If desired, no flange need be added, the container being retained to the vent by some other means. For example, a device 10 having a cylindrical container 14 similar to that shown in FIG. 1 but without the flange 16 is shown in FIG. 2B. The flangless device 10, as shown in FIG. 2, is held to the vent 12 of another manufacturer by a holder 36, here a cage type holder as shown in FIG. 2A. The cage holder itself has a flange 38 for attaching to the vent 12, the pins 24 b of the vent 12 being inserted in the holes 38 and melted to fix the cage with the catalyst device 10 to the vent 12.

[0042] For some battery designs it is not possible to attach the catalyst device to the pressure relief vent. Illustrated in FIG. 3 is the top view of a jar cover 40 for Monoblock type battery cells that have a vent boss 42 into which a pressure relief valve fits. The vent boss of this particular example has an opening 44 which has about a 6 mm diameter, and four recesses 46 around the opening 44. Other vent bosses of other manufacturers may have openings 44 of a different diameter. Shown in FIG. 3A is a smaller version of the catalyst device 10 having a diameter (width) no larger than the vent opening, in this example about 6 mm, for fitting in the opening 44 of the vent boss 42. The container 14 has a non-porous wall 18 and an opening 20 into the chamber 22. In the chamber 22 is a layer of catalyst 26, a layer of filter 28, all of which is sealed from the environment of the battery cell by the micro porous section 30 which is formed as a small micro porous disk member 30 a. Two tabs 48 integrally connected to the container 14 extend therefrom for fitting into the recesses 46 of the boss 42 and holding the device 10 in place when installed in the opening 44 as seen in FIG. 3.

[0043] The configuration shown in FIGS. 3 and 3A is rated at about ¼ Amp, the chamber 22 having a volume of about 0.02 cubic inches, ⅓ to ½ of which is filled with catalyst 26, the rest with filter material 28. The micro porous disk member 30 a being a PTFE disk of roughly 0.02 inches square surface area, ⅛ inches thick, and a pore size of 25 microns allowing 3-6 ml/minutes at standard temperature and pressure of 2 parts H₂ and 1 part O₂ passing through to the catalyst.

[0044] Another option would be to simply drop the catalyst device 10 into a battery cell. A configuration suitable for doing so is shown if FIG. 4. Here the device 10 has a container 14 similar to that of FIG. 1 formed with a series of legs 50 which extend beyond the top end 51 of the container which has the micro porous disk member 30 a so that no matter how the device 10 lands within the battery cell, the micro porous member 30 a will not sit flat against any object which may block the flow of gas.

[0045] With VRLA cells of the Gel type, spitting action within the cell may coat the micro-porous member 30 a with gel and block the gas access to the catalyst depending on how the device 10 is positioned. A shield could be attached as a separate piece or could be part of the molded container itself to protect the porous hydrophobic disk and the catalyst active material from the spitting silica and silica gel. With non Gel cells such as AGM and liquid electrolyte cells, this should not be a problem.

[0046] The catalyst cartridge assembly can be made to have a self-shutdown mode. If the heat of reaction reaches the melting temperature of the plastic used to house the active material, it will melt and physically cover the active material. This physical covering of the active material will block precious metal activation sites, rendering the catalyst ineffective and shutdown the reaction.

[0047] It is seen that the use of catalyst is made safer from the viewpoint that by limiting the temperature of the reaction there is no way that a catalyst of this design could possibly damage the cell, even if the cell is in a high gassing situation such as boost charge, or a cell failure mode. The catalyst is designed to bypass excess gas if the cell is creating more gas than the catalyst has been designed to recombine. This reaction limitation is controlled by the porous section 30 which has a predetermined gas flow rate limit.

[0048] Thus, the present invention can be attached directly to low temperature plastic materials such as polypropylene, ABS and other materials commonly used in batteries. This catalyst can be attached directly to vent caps, or other components of the battery.

[0049] Another alternative embodiment of the present invention is now described with reference to the device 10 of FIG. 5. Unlike the previous embodiment, here, the porous section 30 is in the container wall 18. The device 10 has a cylindrical container 14 having a container wall 18 and defining a chamber 22. An opening 20 provides access to the chamber for adding the catalyst 26. The porous section 30 is provided in at least a section of the wall 18 of the container 14, here the entire wall structure 18 being porous. The container 14 is made of a porous plastic material such as PVDF, Teflon, or Polypropylene. The opening 20 is sealed with a nonporous plug 52 so that the gas or vapor can pass only through the pores in the wall 18. Like the embodiment discussed above, the pore size of the porous section, here the wall 18, is chosen to allow gas to pass, but not liquid, and to prevent a flame front from passing through. Within these parameters, the pore size can be varied to control the amount or rate of gas that can pass through the chamber walls and subsequently be exposed to the catalyst active material, i.e., temperature control. Pore sizes for temperature control are preferably between 1 and 40 microns. Varying the wall thickness of the container in conjunction with the pore size and surface area of the container can also be used to control temperature.

[0050] The non porous plug 52 is preferably made of an epoxy that does not itself exhaust catalyst poisons and which is suitable for the environment in battery cells. Such materials include acrylic based compounds such as Loctite Material 3345 which are cured by Ultra Violet radiation for 15 seconds, or silicon based compounds such as Loctite Material 5091 partially cured by UV for 30 seconds and followed by a secondary moisture cure. A wadding of fiber glass material acts as a dam between the catalyst 26 and the plug 52 when the plug is first poured.

[0051] A thermal mass material 54 may be added with or without temperature control sized pores to also help control temperature. As seen in FIG. 4, the catalyst 26 is mixed with the thermal mass material 54 which can be made of a powder of a ceramic material or a plastic material (e.g., polypropylene, acrylic) or a metal (e.g., aluminum, copper, brass). It is believed that the powdered material should be of a size that is less than or equal to the size of the catalyst material, and that there be about 2 parts thermal mass material to 1 part catalyst material. This design is believed to work by increasing the thermal mass of the chamber, in other words, by spreading the heat of reaction over a larger mass.

[0052] Catalyst poison filter material 28 can also be added to the device 10 of the type shown in FIG. 5. One possibility is to add filter material directly to the plastic material of the container 14. Filter material 28 such as activated carbon can be impregnated into the plastic of the container 14 during the molding process. One way of doing this is to mix the powders of the plastic and the filter materials 28 and then mold the mixture to form the container 14. Pores of the desired size are also added. One example is a mixture of 80% PVDF and 20% activated carbon with K₂CO₃. The addition of the filter material, however, may lesson the hydrophobic nature of the container. A porous PTFE film wrap around the container 14 as disclosed in U.S. application Ser. No. 09/022,336 could be added if desired to increase the hydrophobic nature.

[0053] Another possibility (not shown in FIG. 5) is to mix the filter material 28 with the catalyst 26 in the chamber 22. As discussed above, however, where poisons are not forced first through a filter, poisons that have a high affinity for the catalyst may still poison the catalyst.

[0054] Shown if FIG. 6 is a means of adding poison control to a porous ceramic type container. Here a filter material 28 of K₂CO₃ is coated onto the outside of the container 14. The ceramic container is dipped in a water solution of dissolved filter material and then dried to leave a coating of filter material. The ceramic container is then wrapped in porous PTFE film 56 which acts as the microporous section 30. Other solvent soluble filter materials may be used as well.

[0055] Shown if FIG. 7 is a means of adding filter material to any type container by a wrap. A film 58 impregnated with filter material is wrapped around the outside of the container 14 after it is loaded with catalyst 26 and the opening 20 sealed. This film could be laminated to the back of a porous PTFE film, or installed as a separate film which would require a separate porous PTFE film wrap 56 on top.

[0056] It is seen that an advantageous catalyst device is provided that can be simpler and less costly to produce than previously known devices. Moreover, poison and temperature control functions can be included. The invention also allows for greater flexibility in design of catalyst assemblies to fit a great number of cell designs. For example, the plastic container, whether non-porous or porous, has the advantage of allowing a flange to be added for easy attachment to a pressure relief vent and thereby eliminates the need for holders such as the cage holder even in embodiments where poison and temperature control are not desired. Moreover, the flange can be configured for the relief vent of a particular manufacturer.

[0057] The catalyst device can be added to a battery cell by itself, attached to a pressure relief vent, or some other means of placing the catalyst in contact with the gasses within a battery cell. A VRLA cell 60 is schematically shown in FIG. 8 and has a sealed housing 62, a positive electrode 64 having active material, a negative electrode 66 having active material and which is in spaced relationship to said positive electrode, and an electrolyte in contact with the positive and negative electrodes (normally in the form of plates). The electrolyte may be contained in a separator means so that there is no “free” electrolyte in the cell. The VRLA cell is typically charged on a continuous basis and over a long-term, for example, in excess of five years. The word “continuous” as used herein in connection with the charging of the cell is intended to mean an uninterrupted flow of current, as well as an intermittent flow of current, for example, a pulsating current. A VRLA cell is typically charged at a voltage having a value that is slightly in excess of the value of the open-circuit voltage of the cell which, for example, is typically about 2.15 volts. The term “slightly in excess” means a value no greater than about 0.3 volt above the open circuit voltage of the cell in applications in which there is an intermittent flow of current. In applications in which the flow of current is uninterrupted during charging, it is preferred that the charge voltage have a value that is no greater than about 0.2 volt above the open-circuit voltage of the cell. As discussed above, the catalyst device 10 is ideally attached to the pressure relief vent 12 of the VRLA cell which is positioned in a gas space 68 within the housing where oxygen and hydrogen gas collect. The pressure relief vent 12 allows excess gas to escape the sealed housing and is preferably removable. Thus combining the catalyst device with the relief vent 12 makes the catalyst device removable while assuring it is in contact with the gas for recombination.

[0058] Parameters and Considerations for Sizing Catalysts for VRLA Cells

[0059] It is believe that a standard AGM VRLA cells exhaust 100 ml/day/100 Ah of an oxygen hydrogen mixture at standard VRLA float charging voltages at 90° F. It is further believed that similar AGM VRLA cells with catalyst exhaust 20 ml/day/100 Ah of pure hydrogen (due to positive plate corrosion) at 90° F. Such gassing data indicates the catalyst must recombine 80 ml/day/100 Ah to keep the negative plates of a VRLA battery fully charged.

[0060] The minimum amount of Gas to be Combined: The largest AGM VRLA cell currently known to be produced is 1600 Ah. Faraday's law states that 1 Amp of current used to breakdown water into stoichiometric Hydrogen and Oxygen gas will produce 11.3 ml/min 2H₂−1O₂ at STP. Therefore the catalyst must recombine at most 0.079 amps of gas in a 1600 Ah AGM VRLA cell on float charge at 90° F. (1600 Ah/100 Ah)(80 ml/day/100 Ah)/((11.3 m/min)*(60 min/hr)*(24 hr/day)).

[0061] The amount of gas produced by VRLA cells will change with the cell operating temperature based on Arhennius' equation. This equation shows that the volume of gas recombined by the catalyst will increase or decrease by approximately a factor of 2 for every 10° C. change in temperature. (10° C. rise in temperature will double the amount of gas needed to recombine (80 ml/day/100 Ah@32° C.=160 ml/day/100 Ah@42° C.))

[0062] VRLA cell manufacturers recommend VRLA cells be operated in a climate-controlled environment of 77° F., the 90° F. used for testing and the above data calculations represents a maximum recombination situation.

[0063] Heat Generation: The recombination reaction of oxygen and hydrogen to water will create 275 BTU/ft³ of heat. (1 ft³ of stoichiometric oxy-hydrogen=28310 ml of gas at STP). Therefore catalysts produce 0.073 BTU/min of heat for every 11.3 ml/min (1 amp) of stoichiometric oxy-hydrogen.

[0064] Maximum Steady State Operating Temperature: This 0.073 Btu/min/amp of heat is dissipated from the catalyst to the surroundings through a combination of heat flow release (conduction, convection, radiation). The micro porous disk of the 1 amp catalyst device 10 is specifically designed (by specifying pore size, surface area, thickness, etc.) to allow 11-12 ml/min stoichiometric oxy-hydrogen gas into the catalyst chamber and the resultant water vapor to diffuse out of the chamber. This specified gas flow rate generates the stated 0.073 BTU/min/amp of heat, which is dissipated by the catalyst to it's surroundings resulting in a steady state operating temperature of 120-140° F. measured at the outside surface of the catalyst chamber.

[0065] There is a similar heat generation to operating temperature relationship for the 0.25 amp catalyst device 10. The geometry of the 0.25 amp catalyst device allows between 3 and 6 ml of stoichiometric oxy-hydrogen into the catalyst with resultant water vapor exiting. The recombination of this amount of oxy-hydrogen generates 0.018 to 0.037 BTU/min of heat. This amount of heat generates a steady state operating temperature of 100-120° F. measured on the outside surface the 0.25 amp catalyst chamber.

[0066] The enthalpy generated by the catalyst reaction is a function of the stoichiometric oxy hydrogen gas flow rate through the micro porous membrane, the amount of catalytic material available to react with available gas and the packing density of the catalytic material inside the catalyst chamber.

[0067] The gas flow rate through the micro porous membrane is a function of membrane pore size, porosity, and surface area perpendicular to gas flow and is an inverse function of membrane thickness (defined as the length of the membrane perpendicular to gas flow).

[0068] An example of a properly sized micro porous membrane for this application is the preferred embodiment, using a micro porous PTFE disk with a surface area normal to gas flow of: 0.196 in², a pore size of 25 microns, a porosity of 15% and a thickness perpendicular to gas flow of 0.125 in. This size disk limits stoichiometric oxy-hydrogen gas flow to 10-15 ml/min, which limits the enthalpy generated by the catalyst embodiment to 0.064 BTU/min-0.090 BTU/min.

[0069] Regarding the filter material, the filters may have a finite life of limited capacity to absorb poisons. Thus over the life of the battery, a filter, or the container with the filter, may need to be replaced.

[0070] It is understood that the above-identified arrangements are merely illustrative of the many possible specific embodiments which represent applications of the present invention. Numerous and varied other arrangements can readily be devised in accordance with the principles of the invention without departing from the spirit and scope of the invention. 

What is claimed is:
 1. A device for combining gases within a storage battery; comprising: a catalyst container having a container wall and defining an internal chamber; a catalyst arranged within said chamber, said catalyst capable of reacting oxygen gas and hydrogen gas to form water vapor; a micro-porous section having pores through which said oxygen gas and hydrogen gas can pass between said internal chamber and an outside of said container; and a catalyst poison filter arranged to remove at least a portion of catalyst poisons in said oxygen and hydrogen gas.
 2. A device in accordance with claim 1 wherein said micro-porous section is arranged in at least a portion of said container wall.
 3. A device in accordance with claim 2 wherein said container comprises a plastics material.
 4. A device in accordance with claim 3 wherein said micro-porous section has a pores sized in the range of about 0.1 to about 400 microns.
 5. A device in accordance with claim 3 wherein said filter material is impregnated into said plastic material.
 6. A device in accordance with claim 1 wherein said filter is arranged within said chamber.
 7. A device in accordance with claim 6 wherein said filter is arranged in a layer adjacent to said catalyst.
 8. A device in accordance with claim 1 wherein said container is substantially non-porous and has an opening to said chamber, and wherein said micro-porous section comprises a micro-porous hydrophobic member arranged to seal said opening and having pores of a size to allow gas to pass there through to said chamber.
 9. A device in accordance with claim 1 wherein said poison material comprises activated carbon.
 10. A device in accordance with claim 1 wherein said poison filter comprises potassium carbonate.
 12. A device in accordance with claim 10 wherein said activated carbon is impregnated with potassium carbonate.
 13. A device in accordance with claim 1 further comprising a pressure relief vent.
 14. A device in accordance with claim 1 wherein said container is made of a plastic material and is attached to a flange capable of attaching to a pressure relief vent.
 15. A device for combining gases in a storage battery; comprising: a catalyst container having an internal chamber and an opening to said chamber, said container being substantially non-porous; a catalyst arranged within said chamber, said catalyst capable of reacting oxygen gas and hydrogen gas; a catalyst poison filter arranged within said chamber; and a micro-porous hydrophobic member arranged to seal said opening, said micro-porous member having pores of suitable size to permit gas to pass there through while being a barrier to liquids.
 16. A device for combining gases in accordance with claim 15 wherein said filter is arranged between said catalyst and said micro-porous member.
 17. A device for combining gases in accordance with claim 16 wherein said container comprises a plastic material.
 18. A device for combining gases in accordance with claim 15 wherein said micro-porous member comprises a plastic material.
 19. A device for combining gases in accordance with claim 15 wherein said container is cylindrical, has no more than one said opening, and comprises a plastic material, and wherein said micro-porous member comprises a plastic material.
 20. A device for combining gases in accordance with claim 15 further comprising a pressure relief vent, said container being attached to said pressure relief vent.
 21. A device for combining gases in accordance with claim 15 wherein said container is made of a plastic material and is attached to a flange capable of attaching to a pressure relief vent.
 22. A device for combining gases in accordance with claim 20 wherein said container is supported in a holder attached to said vent.
 23. A device for combining gases in accordance with claim 15 further comprising at least one tab extending from said container, said tab capable of engaging a complimentary recess for holding said housing in place when installed in said storage battery.
 24. A device for combining gases in accordance with claim 20 wherein said housing is snap connected to said vent cap.
 25. A valve regulated lead acid (VRLA) battery cell comprising: a sealed housing; a positive electrode positioned in the housing; a negative electrode positioned in the housing in spaced relationship from the positive electrode; an electrolyte in said housing in contact with said positive and negative electrodes; a gas space within said housing in which oxygen and hydrogen gas collects; a pressure relief vent which allows gas to escape from the housing and which prevents oxygen gas from outside the housing to contact said negative electrode; a catalyst device arranged to be in contact with at least a portion of said oxygen and hydrogen gas, said device including a container having a container wall and defining an internal chamber, and a catalyst arranged within said chamber, said catalyst capable of reacting oxygen gas and hydrogen gas to form water vapor; and a catalyst poison filter arranged to be in contact with at least a portion of said oxygen and hydrogen gas.
 26. A VRLA battery cell in accordance with claim 25 wherein said catalyst device further comprises a micro-porous section arranged to and having pores sized to allow oxygen gas and hydrogen gas to pass from said gas space to said chamber, said micro-porous section being hydrophobic to said electrolyte.
 27. A VRLA battery cell in accordance with claim 26 wherein said poison filter is arranged within said chamber, and said micro-porous hydrophobic section comprises a single piece of plastic material.
 28. A catalyst container for use in battery cells having an electrolyte, said container comprising: a container wall comprising a plastic material; a chamber within said container capable of holding catalyst; and a flange attached to said container.
 29. A container in accordance with claim 28 wherein said container wall has pores of sufficient size to allow gas to pass through to said chamber, and is hydrophobic to said electrolyte.
 30. A container is accordance with claim 28 wherein said container wall is impermeable to gas and liquids, and further includes an opening into said chamber, said opening being sealed with a micro-porous hydrophobic member having pores of sufficient size to allow gas to pass through to said chamber.
 31. In a method for charging a valve-regulated, lead-acid (VRLA) cell at a charge voltage which has a value that is slightly in excess of the value of the open-circuit voltage of the cell, said cell including, in spaced relationship, a positive electrode and a negative electrode, and sandwiched therebetween electrolyte-containing separator means in which electrolyte is contained, wherein, during charging of the cell, there is produced at the positive and negative electrodes respectively oxygen gas and hydrogen gas in a predetermined amount, a portion of the oxygen gas tending to migrate through the electrolyte-containing separator means to the negative electrode and cause depolarization thereof, wherein there is also formed at the positive electrode hydrogen ions which migrate to the negative electrode to form hydrogen gas in an amount less than said predetermined amount, the negative electrode tending to discharge over a prolonged period of time during charging, wherein the tendency of the negative electrode to discharge during charging in inhibited by controlling the amount of oxygen gas in the cell by catalytically converting a portion of the oxygen gas and a portion of the predetermined amount of hydrogen gas to water, and wherein during said catalytic conversion there is a tendency for the reaction to generate heat which affects adversely the operation of the cell, the improvement comprising controlling the reaction to inhibit the generation of excess heat by controlling the amounts of oxygen gas and hydrogen gas that are contacted with the catalyst. 